Tempmax Alumina Fiber Industry Kiln Use Polycrystalline Wool Board

• Usage: High Temperature Insulating Material, Thermal Insulation Material
• Temprature Classification: 1600℃, 1500℃, 1650
• Chemical Composition: SiO2, Al2O3.SiO2, Al2O3
• Shape: Ceramic Fiber Plate
• Manufacturing Technique: Polycrystalline Wool Board
• Kind: Alumina Fiber
• Model NO.: TempMax
• Province: Shandong
• Name: Polycrystalline Wool Board
• Product: Alumina Fiber Board
• Raw Material: Polycrystalline Wool
• Material: Alumina Fiber
• Manufacturer: Luyang
• Transport Package: Carton/Bag/Pallet
• Specification: 12.5mm/25mm/50mm
• Trademark: TempMax
• Origin: China
• HS Code: 68061010
• Production Capacity: 500, 000 Tons

Product Description

 

TEMPMAX^® Thermal Insulation Polycrystalline Wool Alumina Fiber Board / PCW Board

TempMax^® alumina fiber board is manufactured in a wet forming process using TempMax^® alumina fiber bulk and binders. TempMax^® alumina fiber board has excellent thermal stability at very high operating temperatures. TempMax^® alumina fiber board can reduce energy costs and cycling times due to high insulating capability, as well as serving to protect refractory surfaces from thermal shock and chemical attack.

 

Features

Excellent thermal shock resistance

Can be machined, cut and shaped easily

High rigidity and light weight

Low thermal conductivity

Low heat storage

 

Typical Applications

High-temperature laboratory

High-temperature furnaces and kilns

Aerospace industry

Back-up insulation to dense refractory linings

Expansion joints

 

Typical Parameters

Description	TEMPMAX^®  140 BOARD	TEMPMAX^®  145 BOARD	TEMPMAX^® 160 LD BOARD	TEMPMAX^® 160 HD BOARD
Classification Temperature (ºC )	1600	1600	1700	1700
Continuous Temperature Use Limit (ºC )	1400	1450	1600	1600
Chemical Composition (%)
Al2O3	60	62	70	70
Al2O3+SiO2	98	98	98.5	98.5
Color	White	White	White	White
Density (kg/m³)	300	300	250	400
Modules of Rupture (MPa)	≥0.3	≥0.3	≥0.3	≥0.3
Compressive Strength (MPa, 10% relative deformation)	0.25	0.25	0.15	0.3
Loss of Ignition (%)	≤8	≤8	≤8	≤8
Permanent Linear Shrinkage (%)	1400ºC x 24h ≤2.0	1450ºC x 24h ≤2.0	1600ºC x 24h ≤1.5	1600ºC x 24h ≤1.5
Thermal Conductivity (W/m·K)
400ºC	0.08	0.08	0.08	0.08
600ºC	0.10	0.10	0.12	0.09
800ºC	0.13	0.13	0.14	0.12
1000ºC	0.16	0.15	0.17	0.15
1200ºC	0.19	0.19	0.20	0.19