| Usage: | High Temperature Insulating Material |
|---|---|
| Temprature Classification: | 1600℃, 1500℃, 1400℃, 1260℃, 1050℃ |
| Chemical Composition:: | SiO2, Cao, MGO |
| Shape: | Ceramic Fiber Plate |
| Manufacturing Technique: | Thermal Insulation Material |
| Kind: | Ordinary Ceramic Fiber |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier 
Biowool® soluble fiber board is manufactured in a wet forming process using Biowool® soluble fiber bulk and binders. Biowool® soluble fiber board is designed for insulation applications experiencing vibration, mechanical stress and erosive forces. Biowool® soluble fiber board can reduce energy costs and cycling times due to high insulating capability, as well as providing stability to the entire refractory lining system.
Features
Excellent thermal shock resistance
Can be machined, cut and shaped easily
High compressive strength and rigidity
Low thermal conductivity and heat storage
Light weight
Typical Applications
Furnace hot face lining in petrochemical furnace
Furnace hot face lining in ceramic kiln
Back-up insulation to dense refractory linings
Molten metal transfer
Expansion joints
Typical Parameters
|
Description |
BIOWOOL® 1100 BOARD |
BIOWOOL® 1300 BOARD |
|
Classification Temperature (ºC ) |
1100 |
1300 |
|
Color |
White |
White |
|
Density (kg/m³) |
300 |
300 |
|
Modules of Rupture (MPa) |
≥0.25 |
≥0.25 |
|
Compressive Strength (MPa, 10% relative deformation) |
0.15 |
0.15 |
|
Loss of Ignition (%) |
≤7 |
≤7 |
|
Permanent Linear Shrinkage (%) |
1000ºC x 24h ≤2.0 |
1260ºC x 24h ≤2.0 |
|
Thermal Conductivity (W/m·K) |
||
|
200ºC |
0.05 |
0.05 |
|
400ºC |
0.08 |
0.07 |
|
600ºC |
0.11 |
0.10 |
|
800ºC |
0.12 |
0.11 |
|
1000ºC |
0.15 |
0.14 |